Jaysuing Invisible Waterproof Agent

1, waterproof mortar construction: clean up the basic sediment, debris, oil, etc.;

The cement-sand ratio is controlled in 1:2.5~3(32.5r grade Portland cement, medium sand, mud content is less than 3%), water cement ratio is less than 0.5. Pure silicone waterproofing agent dosage of cement dosage of 3~5%, in order to ensure the mixing, should be the first silicone waterproofing agent and mortar ratio of water mixed evenly and then add cement and sand. The waterproof layer is divided into two layers (each layer is 10mm thick).

The bottom layer is first plastered with vegetable mortar 1mm, and then plastered with waterproof mortar layer. When the initial setting, it is compacted and rubbed into pitted surface with wood trowel. Wipe the second layer of waterproof mortar after pressing smooth compaction (such as decoration construction, must be rubbed intohemp).

According to the normal water spraying curing, spraying cement curing agent effect is better.

 2, waterproof concrete construction: pure silicone waterproof dose accounted for 1% of the cement dosage, evenly mixed with thepreparation of concrete, and ordinary concrete construction method is the same.In order to ensure that the mixture is uniform, should first be organic silicon water-proofing agent and concrete with a proportion of water mixed evenly and then add cement, sand and stones.

 3, leakage maintenance construction: the original base smooth surface should be chiselled into the pitted surface, after cleaning the floating ash, do the plain mortar combination layer, and then wipe the waterproof mortar layer.

Is the leaking place must first stop the water.

The Angle of Yin and Yang should be rounded and compacted.

Stubble to slope shape (stubble width 100~150mm), stubble with plain mortar as a binding layer, and then wipe waterproof mortar layer.

 4, spraying impermeable construction: silicone waterproof agent plus 15 times water diluted after spraying on cement surface,brick, tile, gypsum board, ordinary coating wall and other absorbent inorganic building materials surface for impermeable moisture-proof treatment, has excellent effect.